Description
K316LT is designed for MAG welding of low carbon 18%Cr-12%Ni-2%Mo stainless steels and this wire has low carbon content which gives goof resistance to most types of corrosion of the weld metal
Wire is titania type of flux cored wire for all position welding and the weld metal contains optimum ferrite contents in their austenitic structures, excellent weldability and increased creep resistance and elevated temperature
Classifications
EN ISO 17633-A:2008
: T46 0 P C H10
KS D 3612
: YF-316LC
EN ISO 17633-B:2008
: T49 0 T1-1CA-U H10
JIS Z 3323
: TS316L-FB1
AWS A5.22-07
: E316LT-1/4
Composition(%)
C
0.03
Si
0.60
Mn
1.15
Cr
19.50
Ni
12.70
Mo
2.4
FN
7.5
Shielding gas
CO2
Mechanical
Y.S
T.S
EI.
AWS A5.22
Min 485
Min 30
EN ISO 17633-B
Min 320
Min 510
Min 25
Example
420
560
38
Package
Dia (mm)
0.9
1.2
1.6
Spool (kg)
5, 12.5, 15
Notes on usage welding condition
When heat input is excessive, base metal will be bended or distorted due to the bad heat conductivity. Therefore, perform welding with select proper heat input